Product Description 
 Two component, high performance surface coating materials, coating, or spray can spray .5811 brush can make the surface from chemical corrosion, wear and erosion from water solution. Application: 
 Submersible pump cooling tower 
 Sea water tanks and channel buoys 
 Storage tank water tank 
 Manhole pipe inside and outside surface 
 Steel piles and concrete pile water filter 
 Regional wastewater treatment chemical seal 
 Underground pipeline structure 
 6: Physical / mechanical properties 
 At 25oC, the curing can be determined after 7 days or 24 hours at 25oC before curing, to cure 4 hours when 100oC. 
 Adhesion 
 Tensile shear 
 By ASTM D1002 test, blasting 0.075-0.08mm, its typical value is: 
 Natural curing heat cure 
 Al 113kg/cm2 159kg/cm2 
 Brass 180kg/cm2 181kg/cm2 
 Low carbon steel 190kg/cm2 233kg/cm2 
 Copper 133kg/cm2 147kg/cm2 
 Stainless steel 177kg/cm2 178kg/cm2 
 Lance Stuart test 
 According to NACE TM01-74 test samples in water at 60oC 1680 hours when soaked soaked parts of no visible bubbles. 
 Anti-chemical corrosion 
 Once fully cured, the material below has excellent resistance to chemical corrosion: 
 10% methanol, sulfuric acid 
 20% 10% phosphoric acid hydrochloric acid 
 Sodium acetate 
 Ammonia 25% ethylene glycol 
 Diethanolamine salt water 
 Water oil 
 Gasoline (oil) Mineral oil 
 Compressive strength 
 Tested by ASTM D695, the typical value is 
 476kg/cm2 natural cure 
 613kg/cm2 heat cure 
 Flexural strength 
 Tested by ASTM D790, the typical value is 
 283kg/cm2 natural cure 
 407kg/cm2 heat cure 
 Hardness 
 Tested by ASTM D2240, Shore hardness 
 Natural Cure 
 Heat cure 
 Impact strength 
 Tested by ASTM D256, Izod impact strength: 55 J / m.